Abstract
The friction reduction mechanism of glycerol monooleate (GMO) was investigated under boundary lubrication with elevated temperature. Tribological performances were tested using reciprocating test rig by adding 5 wt.% GMO into Poly-alpha Olefin (PAO) base oil. Friction coefficient and wear were recorded during experiments. The used oil was evaluated by infrared detection after experiments. Results show that GMO could reduce friction coefficient at both low and high temperature. At elevated temperature, the friction coefficient of PAO-GMO blend climb up gradually, followed by a decrease tendency, and the wear increase gradually with temperature. The results of Quartz Crystal Microbalance show that the physical adsorption film plays the main role in friction reduction at low temperature. While at high temperature, the Infrared Spectrum and X-Ray Photoelectron Spectrum show that the GMO involves into the chemisorption with friction surface, producing Fe(OH)O and Fe3O4. The friction reduction mechanism of GMO transferred from physisorption to chemisorption, which reduced friction coefficient at both low and high temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.