Abstract
The fretting wear behaviors and wear mechanism of the Cr-coated Zr–1Nb alloy cladding tube mated with Zr-4 alloy dimple were investigated under different tangential displacements. With the increasing tangential displacement, the fretting running status changes from mixed fretting regime to gross slip regime, the friction coefficient increases first and then decreases, and the removed material volume, maximum wear depth, and wear coefficient of the Cr-coated Zr–1Nb alloy cladding tube increase. Fouvry's criteria were used to verify the correctness of the fretting running status. The primary wear mechanisms in the mixed fretting regime are adhesive wear and oxidative wear, while those in the gross slip regime are delamination wear and oxidative wear. The wear mechanism of the dimple is mainly delamination wear. Cr coating inhibits the wear of the cladding tube. After the coating is completely removed, the volume of material removed from the cladding tube increases dramatically, eventually exceeding the volume of material removed by dimple.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.