Abstract
In this study, the ambient temperature fretting wear behavior and the wear mechanisms of the Selective Laser Melting prepared IN738LC alloy with various micro-structures were systematically investigated under varying load conditions (35 N, 100 N). The results indicate that the running states of fretting gradually transitions from the gross slip regime (GSR) to the mixed slip regime (MSR) as the load increases. The HT-2 samples (Unimodal precipitation, hardness 512 HV) present more fine homogeneous and dense secondary γ′ phase compared with HT-1 (Bimodal precipitation, hardness 487 HV) and As-built (No precipitation, hardness 392 HV) counterpart, which result in excellent wear resistance. The main fretting wear mechanisms for all samples were oxidation wear, abrasive wear, fatigue wear.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.