Abstract
Effect of mean stress on fretting fatigue behavior of 304 austenitic stainless steel has been investigated by conducting fretting fatigue tests at a constant contact pressure of 100 MPa under three different mean stresses i.e., 0, 350 and 450 MPa. For comparisons, plain fatigue tests were also carried out. The influence of tensile overload on fretting fatigue life was also investigated. The results showed that with an increase in mean stress, the reduction in fatigue strength due to fretting increased drastically from 51% at 0 MPa mean stress to 71% at 450 MPa mean stress. The application of tensile overload during fretting fatigue had significant influence on the fretting fatigue lives when the tensile overload was above yield strength. The fretting variables, i.e., tangential stress and relative slip amplitude were measured during fretting fatigue tests. Fracture surfaces were examined using scanning electron microscope. The results have been discussed based on the tangential stress measurement, relative slip amplitude evaluation during fretting fatigue and fracture surface examinations.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.