Fretting crevice corrosion of stainless steel stem–CoCr femoral head connections: Comparisons of materials, initial moisture, and offset length

Abstract

Modular tapers continue to be used in a wide variety of orthopedic implants. In this study, stainless steel (ASTM F-1568) femoral hip stems combined with Co-Cr-Mo alloy heads (SS/CoCr) were tested in an in vitro fretting corrosion test set-up to assess the propensity for mechanically assisted corrosion. Three different aspects of the modular design were evaluated in this study: (1) material combination compared to CoCr/CoCr, (2) wet versus dry assembly for SS/CoCr couples, and (3) 0- and 6-mm head offset for SS/CoCr couples. Fretting corrosion tests over a range of cyclic loads up to 3300 N were performed, and continuous cyclic loading at 3300 N for 1 M cycles were performed on each group (n = 5). Fretting micromotion was measured as a function of cyclic load on select couples to detect the nature and extent of motion present. The results showed that SS/CoCr couples were more susceptible to fretting corrosion than CoCr/CoCr couples, that dry assembly does not prevent fretting corrosion from taking place but raises the onset load, and that 6-mm offset heads had higher visual evidence of fretting damage but showed mixed statistical results in terms of onset loads and OCP shifts and currents compared to the 0-mm offset samples. Current and voltage excursions over 1 million cycles tended to diminish towards their unloaded control levels but did not fully recover until cyclic loading ceased. Micromotion measurements indicated fretting motions in the range of 10-25 microm where 0-mm heads tended to piston on the trunion, while 6 mm heads tended to rock.