Abstract
Five samples of mixed Y 2 O 3/ CaO doped ZrO 2 electrolytes, with the same nominal chemical composition of ( ZrO 2)0.90–( Y 2 O 3)0.04-( CaO )0.06, were sintered at 1600°C for 2, 4, 6, 8 and 10 h, respectively. The frequency dependence of the grain-boundary conductivity of each sample was measured using complex impedance method in the temperature range from 773 to 1073 K and experimental results were analyzed according to a power law, which was frequently referred to as the so-called universal dynamic response (UDR). Results indicated the apparent ac grain-boundary conductivity can be well-described by the power law and some useful information about the grain-boundary effect, such as the activation energy of the grain-boundary conduction and the dissociated energy of the charge carrier in the space charge layer, can be obtained by analyzing the temperature dependence of the power law parameters.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.