Free Na and Less Fe Compositions of SiO<sub>2</sub> Extracted from Rice Husk Ash as the Silica Source for Synthesis of White Mineral Trioxide Aggregate

Abstract

In this research, we report the use of free sodium and less Fe ion silica (SiO2) for preparation of White Mineral Trioxide Aggregate (WMTA). SiO2 was extracted from rice husk ash (RHA) using NaOH 2 M and HCl 37% (v/v) and removal of Na was performed by washing the extracted SiO2 using deionized water with various volumes and techniques. Before extraction, RHA was calcined at a temperature of 700 °C for 3 h. Preparation of WMTA began with mixing the extracted SiO2 20%, CaO 60%, Al2O3 2%, and Bi2O3 18% (w/w). The mixture was calcined at temperatures of 1100 °C for 4 h, grounded to produce WMTA 200 mesh in size and then was characterized using Fourier Transformed Infrared (FTIR) spectrophotometer, X-ray Diffraction (XRD) and Scanning Electron Microscopy-Energy Dispersion X-ray (SEM-EDX). The WMTA characteristics were compared to that of the commercial WMTA ProRoot. The result shows that the silica that was potential as the silica source for WMTA preparation was extracted from RHA involving sonication and washing with 360 mL of deionized water per 10 g of RHA. It contained SiO2 of 94.2%, Fe2O3 of 0.03%, no Na2O, and the particle size of 1.51±0.46 µm. The characterization of WMTA shows that produced WMTA contained tricalcium silicate (C3S), dicalcium silicate (C2S), tricalcium aluminate (C3A) and BiO2, which is comparable to the commercial WMTA ProRoot.