Abstract
Franklinite-zincochromite-gahnite solid solutions were prepared using ceramic or coprecipitation methods, and their pigmenting capacity as cool ceramic pigments in different glazes (double and single firing frits and porcelain frit) was studied. XRD, UV–Vis–NIR diffuse reflectance, CIEL*a*b* colour analysis, band gap measurements, and the photocatalytic degradation of Orange II were carried out to characterise the samples. The following criteria for high red colouring capacity and high NIR reflectance at the minimum Cr amount were found to be the optimal compositions for an intense reddish cool pigment: Zn(Fe1.8Cr0.2), Zn(Al1.5Cr0.5) and Zn(Al1.3Cr0.5Fe0.2)O4. All the powders showed a direct semiconductor behaviour, with a band gap of approximately 2 eV, which fell in the visible range (620 nm); the visible light photocatalysis of Orange II was moderate, but franklinite-zincochromite Zn(Fe1.8Cr0.2) stood out compared with silver orthophosphate.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.