Abstract
Yttria-ceria-doped tetragonal zirconia ((Y, Ce)-TZP)/alumina (Al2O3) composites were fabricated by hot isostatic pressing (HIP) at 1400–1600 °C and 147 MPa for 30 min in Ar gas using fine powders prepared by hydrolysis of ZrOCl2 solution. The mechanical properties of these ceramic composites were evaluated. The fracture toughness and bending strength of the composites consisting of 25 wt% Al2O3 and tetragonal zirconia with compositions 4 mol% YO1.5-4 mol% CeO2-ZrO2, 2.5 mol% YO1.5-4 mol% CeO2-ZrO2 and 2.5 mol% YO1.5-5.5 mol% CeO2-ZrO2 fabricated by HIP at 1400 °C were 6–7 MPa m1/2 and 1700–1800 MPa. Fracture toughness, strength and hardness of (Y, Ce)-TZP/Al2O3 composites were strongly dependent on HIP temperature. The fracture strength and hardness were increased, and grain growth of zirconia grains and phase transformation from the tetragonal to the monoclinic structure of (Y, Ce)-TZP during HIP in Ar at high temperature (1600 °C) were suppressed by the dispersion of Al2O3 into (Y, Ce)-TZP.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.