Abstract
Accelerated thermal aging tests were performed at 400 °C for nearly 18,000 h on Z3CN20.09M cast stainless steel which was used for primary coolant pipes of nuclear power plants. A series of Charpy impact tests were conducted on Z3CN20.09M after different long-term thermal aging time. The test results indicated that the Charpy impact energy of Z3CN20.09M cast stainless steel decreased rapidly at an early stage and then almost saturated after thermal aging of 10,000 h. Furthermore, J-resistance curves were measured for CT specimens of longitudinal and circumferential pipe orientations. It showed that there was no obvious difference in the fracture characteristics of Z3CN20.09M in different sampling directions. In addition, the observed stretch zone width (SZW) revealed that the value of initiation fracture toughness J SZW was significantly lower than that of fracture toughness J IC, indicating a low actual crack initiation energy due to long-term thermal aging.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.