Abstract
A fine-grained TiAl alloy with a composition of Ti-45Al-5Nb-1.5Cr-0.2W (mole fraction, %) with multiphases was prepared by spark plasma sintering (SPS) and heat-treating at 1 100 °C for 48 h. The relationship among sintering temperature, microstructure and fracture toughness were investigated by X-ray diffractometry (XRD), optical microscopy (OM), scanning electron microscopy (SEM) and mechanical testing. The results show that microstructure of the bulk alloy depends on the sintering temperature strongly, and the main phase TiAl and few phases Ti3Al and niobium solid solution (Nbss) are observed in the SPS bulk samples. In the heat-treatment condition, the lamellar and Nbss phase can provide significant toughening by plastic strengthening, interface decohension, crack branch and crack bridge mechanisms. The fracture mode of the SPS TiAl composite samples is intergranular rupture and cleavage fracture.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.