Abstract
AbstractEffect of loading rate on toughness characteristics of hybrid rubber‐modified epoxy was investigated. Epoxy was modified by amine‐terminated butadiene acrylonitrile (ATBN) and recycled tire. Samples were tested at various loading rates of 1–1000 mm/min. Fracture toughness measurements revealed synergistic toughening in hybrid system at low loading rates (1–10 mm/min); hybrid system exhibited higher fracture toughness value in comparison with the ATBN‐modified resin with same modifier content. However, synergistic toughening was eliminated by increasing the loading rate. At higher loading rates (10–1000), the fracture toughness of hybrid system decreased gradually to the level lower than that of ATBN‐modified epoxy. Fractography of the damage zones showed the toughening mechanisms of ATBN‐modified system was less affected by increasing the loading rate compared to that of hybrid system. © 2012 Wiley Periodicals, Inc. J Appl Polym Sci, 2012
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.