Abstract
Aim of the current study is to analyze the fracture toughness values along with other mechanical properties and correlating the microstructures of ultrafine grained (UFG) microalloyed and interstitial free (IF) steels produced through advanced 3-steps control multiphase rolling. The analysis of fracture toughness was carried out through computing KQ (conditional fracture toughness), J-integral (crack initiation energy) and Kee (equivalent energy fracture toughness) values from 3-point bend test data of rolled specimens. Microstructural analysis was performed through transmission electron microscopy (TEM) along with selected area electron diffraction (SAED) and Electron backscatter diffraction (EBSD). The quantitative measurement of low and high angle grain boundaries and their distribution in the deformed state were determined through EBSD analysis. The good combinations of fracture toughness, yield strength (YS) and percent elongation (%El.) (i.e. ductility) were achieved through innovative 3-phase control rolling (microalloyed steel: Kee = 68.9MPa√m, J = 81.4 kJ/m2, YS = 923MPa, %El. = 13.6; IF steel: Kee = 72MPa√m, J = 87.7 kJ/m2, YS = 623Mpa and %El. = 19). This is ascribed to the development of homogeneously distributed submicron size (0.69μm) ferritic + martensitic structure in the microalloyed steel and submicron size (0.83μm) ferritic grains along with high density dislocation substructure in the IF steel. These dislocation cells and substructures could effectively block the crack initiation and propagation. The development of UFG microstructure has been analyzed in the light of deformation induced ferrite transformation (DIFT) and dynamic recrystallization (DRX) mechanisms. Superior fracture toughness of the UFG steels along with better combination of mechanical properties is very demanding for high strength structural applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.