Abstract
Dissimilar metal welding is seeing growing adoption across industries to enhance structural functionality and efficiency. Achieving high-quality, defect-free dissimilar weld joints requires a comprehensive understanding of the interrelationships between the welding-induced microstructural changes and the material's performance characteristics, particularly its fracture-related properties. This study investigates the impact of microstructural changes on the fracture toughness of dissimilar welds between structural low-carbon steel (S355J2) and austenitic stainless steel (SS316L) prepared using the Rotary Friction Welding (RFW) technique. Welding preforms were created from respective pipe pup pieces. The evaluation involves microstructural analysis, tensile testing, hardness testing, and fracture toughness testing using compact tension specimens derived from various zones of the weld joints. Results revealed significant microstructural differences across the weld joint. The weld region exhibited stable hardness with a maximum of 208 HV1 in S355J2′s thermo-mechanically affected zone (TMAZ). High tensile strength (Ultimate Tensile Strength 540 MPa, Yield Strength 367 MPa) with failures mainly on the S355J2 side. The fracture toughness (KQ) matched parent metal values, with the RFW weld centre line (WCL) showing superior crack tip opening displacement (CTOD) of 0.35 mm. Fractography generally indicates ductile failure.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.