Fracture strength of root filled premolar teeth restored with silorane and methacrylate-based resin composite

Abstract

ObjectivesTo compare fracture characteristics of root-filled teeth with variable cavity design restored with a low shrinkage silorane and methacrylate-based resin composite. Methods77 extracted maxillary premolars were divided randomly into seven groups: (Group 1) intact teeth; (Groups 2–4) MOD plus endodontic access with the buccopalatal width of the occlusal isthmus equals one third of the intercuspal width; (Groups 5–7) MOD plus endodontic access with the buccopalatal width of the occlusal isthmus equals one half of the intercuspal width. Groups 2 and 5 were left unrestored, Groups 3 and 6 were restored with a silorane-based resin composite (Filtek P90) and Groups 4 and 7 with a methacrylate-based resin composite (Z250). Teeth were loaded in a universal testing machine; load and fracture patterns were recorded and compared statistically using 2-way ANOVA and t-test for pairwise comparisons and 1-way ANOVA with Dunnett test for multiple comparisons. ResultsUnrestored teeth became progressively weaker with more extensive preparations, Group 5 (unfilled ½) showed the lowest fracture load among the groups (71±22N, P<0.001). Restorations increased the fracture strength of unrestored teeth regardless of cavity size (P<0.001), but was still significantly weaker than sound teeth, with no significant difference between silorane and methacrylate groups. Failure of restored teeth was mostly adhesive at the tooth restoration interface. ConclusionsSilorane-based resin composite have no superior strengthening effect over the conventional methacrylate-based resin composite in restoration of root filled teeth. Both materials showed similar fracture patterns. Clinical significanceRoot filled teeth are considerably weakened via restorative and endodontic procedures. A direct adhesive restoration will aid in preserving tooth structure as far as it provides enough strength.