Fracture Resistance of Endodontically Treated Maxillary Premolars Restored With Different Methods.

Abstract

The purpose of this in vitro study was to evaluate the resistance and patterns of fracture of endodontically treated maxillary premolars (ETPs) restored with different methods. Mesio-occluso-distal cavities were prepared in 50 extracted caries-free human maxillary premolars after endodontic treatment. The teeth were divided into five groups (n=10), according to the restorative method. G1: intact teeth (control group); G2: conventional composite resin; G3: conventional composite resin with a horizontal glass fiber post inserted between buccal and palatal walls; G4: bulk-fill flowable and bulk-fill restorative composites; and G5: ceramic inlay. For direct restorations, Filtek Z350 XT, Filtek Bulk Fill Flowable Restorative, and Filtek Bulk Fill Posterior Restorative were used. Indirect restorations were fabricated from a pressable lithium disilicate glass-ceramic (IPS e-max Press) and adhesively cemented (RelyX Ultimate). All specimens were subjected to thermocycling (5°C to 55°C/5000 cycles) and additionally submitted to cyclic loading 50,000 times in an Electro-Mechanical Fatigue Machine. Next, the specimens were subjected to a compressive load at a crosshead speed of 1 mm/min until fracture. The fractured specimens were analyzed to determine the fracture pattern using a stereomicroscope, and then representative specimens were carbon coated to allow for the studying of the fracture surface under scanning electron microscopy. One-way analysis of variance (ANOVA) was used to compare fracture resistance of the groups. The results of fracture patterns were submitted to the Fisher exact test (α=0.05). All specimens survived fatigue. Mean (standard deviation) failure loads (N) for groups were as follows: G1: 949.6 (331.5); G2: 999.6 (352.5); G3: 934.5 (233.6); G4: 771.0 (147.4); and G5: 856.7 (237.5). The lowest fracture resistance was recorded for G4, and the highest ones were recorded for G2, followed by that of G1 and G3. One-way ANOVA did not reveal significant differences between groups ( p>0.05). The highest repairable fracture rates were observed in G1 (100%) and G3 (80%). ETPs restored with conventional composite resin with or without horizontal fiber post, bulk-fill composite, and ceramic inlay showed fracture resistance similar to that of sound teeth. Conventional composite resin restorations exhibited the highest prevalence of unrepairable fractures, and the insertion of a horizontal fiber post decreased this prevalence. Intact teeth showed 100% of repairable fractures. It is difficult to extrapolate the results directly to a clinical situation due to the limitations of this study.