Abstract
Objectives: The aim of this study was to evaluate fracture resistance of incisal edge fractures (Class IV) restored with a Glass Fiber-reinforced Composite (FRC). Materials and Methods: Twenty-four extracted sound maxillary central incisors were randomly divided into two groups. Group I (control) contained untreated teeth. Samples in experimental groups II were prepared by cutting the incisal (one-third) part of the crown horizontally and was subjected to enamel preparations, then restored with a Glass FRC. Fracture resistance was evaluated as Newton's for samples tested in a Hounsfield universal testing machine. Failure modes were examined microscopically. Results: Mean peak failure load (Newton's) observed in Glass Fiber-reinforced Nanocomposite was 863.50 ± 76.12. The experimental group showed similar types of failure modes with the majority occurring as cohesive and mixed type. 58% of the teeth in Glass FRC group fractured below the cementoenamel junction. Conclusion: Using Fiber reinforced composite substructure under conventional composites in Class IV restorations, the fracture resistance of the restored incisal edge could be increased.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.