Abstract
The oxidation behaviour of a slip cast, yttria-doped, sintered reaction-bonded silicon nitride after “flash oxidation’ was investigated. It was found that both the static oxidation resistance and flexural stress rupture life (creep deformation) were improved at 1000° C in air compared to those of the same material without flash oxidation. Stress rupture data at high temperatures (1000 to 1200° C) are presented to indicate applied stress levels for oxidation-dependent and independent failures.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.