Abstract
Zinc-coated ultra-high-strength steel (UHSS) sheets are highly susceptible to liquid metal embrittlement (LME) during resistance spot welding. However, systematic understanding on LME cracks in the pullout fracture of UHSS welds is still lacking. This study employs artificially created pre-cracks on bare DP980 steel welds to simulate the LME cracks, allowing accurate control of the crack shape and location. To investigate the fracture initiation and propagation behavior of welds with various pre-crack characteristics, a combined experimental and computational approach, which incorporated tensile tests on newly designed miniature specimens for detailed mechanical property measurement and fracture parameter calibration of different weld zones, was proposed. Results indicate that external pre-cracks in a highly strained region accelerated damage accumulation at the fracture onset region and deflected the fracture propagation path to pass through the pre-crack, causing a 12.1% loss of tensile-shear peak load. Conversely, internal pre-cracks vary the fracture initiation site and exhibit a more detrimental influence, with 24.1% loss of tensile-shear strength. The effects of the pre-crack length, orientation, and depth on the tensile-shear performance were quantified. Results show that the negative effect of the LME crack on the weld performance can be mitigated or avoided by controlling the crack location and geometry.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.