Abstract
Nucleation of microcracks can be detected and analyzed by acoustic emission (AE), by which crack kinematics of locations, types and rientations are quantitatively estimated. The procedure was applied to clarify mechanisms of corrosion cracking. Based on fracture mechanics, numerical analysis was conducted by the boundary element method (BEM). Relations between the stress intensity factors and crack types were investigated by BEM solutions. In experiments, four types of crack patterns were nucleated by employing expansive agent. Following the surface crack, the diagonal crack and/or the horizontal crack propagated. The internal crack extended after the surface crack was terminated. Depending on the crack types, contributions of mode-I and mode-II were varied. According to AE results, four crack patterns observed differently consisted of tensile, mixed-mode and shear cracks. It is demonstrated that mechanisms of corrosion cracking in concrete are dominantly of mode-I failure along with a minor contribution of mixed-mode and mode-II.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.