Abstract
Fracture indentation was applied to estimate the fracture toughness of AISI 1018 borided steels. The Fe2B hard layers were formed using the powder-pack boriding process for two temperatures with 4 and 8 h of exposure times. The fracture toughness of the iron boride layer of the AISI 1018 borided steels was estimated using a Vickers microindentation induced-fracture testing at distances of 15 and 30 m from the surface, applying four loads (0.49, 0.98, 1.96 and 2.9 N). The microcracks generated at the corners of the Vickers microindentation were considered as experimental parameters, which are introduced in a Palmqvist crack model to determine their corresponding fracture toughness KC. As a result, the experimental parameters, such as exposure time and boriding temperature are compared with the resulting fracture toughness of the borided phase.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.