Abstract
Additively manufactured a low carbon Fe–Cr–Ni–Al Corrax stainless steel has ultra-high strength, but the mechanism at work when the steel cracks is still unclear. In this study, Corrax stainless steel was tensile tested to fracture and cracks in the vicinity of the fracture surface were analyzed by scanning electron microscope and electron-backscattered diffraction. The results show that the cracks propagated at angles of 45–60° to the tensile axis. Some cracks were transgranular, and high-angle grain boundaries had little effect on crack propagation. Crack propagation was inhibited in regions with lower Taylor factors. Kernel average misorientation value analysis established that the crack propagation process is accompanied by significant plastic deformation. The influence of particles and unfused pores on crack propagation is also discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.