Abstract
Fractography of stress corrosion cracking (SCC) of 20% cold worked Type 304 H stainless steel containing δ-ferrite was studied using a compact tension (CT) specimen in oxidizing primary water with a scanning electron microscope (SEM) and electron back scattered diffraction (EBSD). The stress corrosion crack propagated mostly in transgranular stress corrosion cracking (TGSCC) mode and sometimes in intergranular stress corrosion cracking (IGSCC) mode. TGSCC paths were along the {111} plane with both high resolved shear stress and high resolved tensile stress. IGSCC preferentially propagated along the grain boundary perpendicular to the loading axis. The findings in this work suggest that TGSCC proceeds through formation of a weakening zone at the head of the crack tip by interaction of slip and corrosion and then cracking of the weakened zone by tensile stress.
Published Version (
Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.