Abstract
AbstractResidues from footwear roughing and carding operations represent 5–15% (w/w) of the solid wastes generated by shoe‐making companies. These wastes are mainly composed by chromium tanned leather and sole materials, and are mostly land filled. Sometimes leaching tests show these wastes as hazardous due to chromium in the leachate. This work aims at a more sustainable option for these wastes by recycling them in styrene butadiene rubber (SBR) and acrylonitrile butadiene rubber (NBR). Thus, they were charged with: (i) ≤1 mm leather waste fibers in the range of 10–25 parts per hundred parts of rubber (phr); and (ii) leather and soles industrial carding and roughing wastes in the range of 20–100 phr. The leather waste fibers‐rubber composites tear strength is increased till 25 phr and both tension and elongation at break decrease within the acceptable range till 12.5 phr for SBR and 15 phr for NBR. In the case of leather and sole carding and roughing wastes, composites tear strength increases till 100 phr, and tension and elongation decrease within the acceptable range till 20 phr. The composite materials at the end of their life cycle may be considered inert or non‐hazardous wastes. POLYM. ENG. SCI., 2011. © 2011 Society of Plastics Engineers
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.