Abstract
Due to the large difference in atomic size between Zr and Nb, TiVNbZr high entropy alloy possesses greater lattice distortion. The change of Zr content can affect the stability of hydrides, which can have an important impact on the hydrogen storage performance. In order to explore the effect of Zr/Nb on hydrogen storage properties, Ti32.5V27.5Nb40-xZrx (x = 7.5, 10, 12.5, 15) high entropy alloys composed of BCC phase are designed. It is found that with the increase of Zr/Nb, the dendritic microstructures first disappear and then gradually become coarse. The Zr-rich BCC phase and the Nb-rich BCC phase appear in the interdendritic and dendritic regions, respectively. Ti32.5V27.5Nb25Zr15 shows excellent activation performance, which is related to the Zr-rich BCC phase with the most catalytic phase on the surface. The hydrogen storage performance of low Zr/Nb composition is better at low temperature, and that of high Zr/Nb composition becomes better after rising to high temperature. This is because with the change of Zr/Nb, low temperature can promote the hydrogen absorption reaction and high temperature can increase the diffusion rate of hydrogen atoms in the interstitial positions of the alloy. Ti32.5V27.5Nb32.5Zr7.5 achieves the best hydrogen absorption capacity of 1.71 wt % at 150 °C. All components undergo a transition from the BCC phase to the FCC phase during the hydrogen absorption process, and then change to a single-phase BCC structure after dehydrogenation. With the increase of Zr content, the first step desorption temperature raises in turn, owing to the stronger thermal stability of hydride.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.