Abstract
Preparation of Y2Ba4Cu7Oy (247 phase) was examined at 1 atm of oxygen partial pressure under the following conditions; (l)using NaNO3 as a reaction accelerator, (2)without reaction accelerator and without seed and (3)using the seeding method, respectively. They were pressed and fired at 850–900°C under oxygen gas flow. The 247 phase was obtained in the temperature range from 860°C to 890°C using NaNO3. Under the condition(2), however, the 247 phase could not be formed in the same temperature range. But, the seeding method was effective; the 247 phase formed at the temperature range from 870°C to 890°C. The sample of the 247 phase prepared at 870°C under the condition(1) exhibited superconductivity with zero resistive point at 93 K.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.