Abstract
Microarc oxidation (MAO) was performed for pure Ti and Ti–6Al–4V alloys, respectively to evolve porous titanium oxide (TiO 2:titania) films at their surfaces. X-ray diffraction (XRD) analysis results reveal that TiO 2 films formed on pure Ti and Ti–6Al–4V alloys have high content of anatase with small content of rutile phases, which would be ideal for high-performance photocatalytic properties. The rutile content was gradually increasing with MAO time period for Ti alloys, while that was almost constant value of 10 vol% for pure Ti. Scanning electron microscopy (SEM) images of the films show uniformly distributed pores for both pure Ti and Ti–6Al–4V alloys. The pore density was higher for pure Ti from 10 min MAO and the pore size became larger for Ti–6Al–4V alloys after 40 min MAO. Microarc oxidized pure Ti showed relatively higher photodecomposition efficiency compared to Ti–6Al–4V alloys, possibly due to the large surface area coming from high porosity and optimum composition of anatase and rutile phases.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.