Abstract
The processing variables that contributed to the formation of subsurface crevices under cerium-based conversion coatings on AA 2024-T3 were investigated. Focused ion beam milling revealed the presence of subsurface crevices underneath a small fraction (∼ 10%) of coated areas, typically in areas with large cracks through the coatings. A solution of sodium chloride and H 2 O 2 etched AA 2024-T3 and produced features similar to subsurface crevices, which confirmed that crevices formed during deposition due to the composition of the coating solution. Using sodium nitrate in place of sodium chloride resulted in no etching of the substrate. Thus, coatings free of subsurface crevices could be produced by using cerium nitrate instead of cerium chloride in the coating solution. Electrodeposited coatings, even those deposited from solutions containing chloride ions and H 2 O 2 , were also free of subsurface crevices. As a result, subsurface crevices are not inherent to cerium-based conversion coatings, but rather were formed due to certain process parameters, specifically the presence of chloride ions and hydrogen peroxide in the coating solution.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.