Abstract
This work reports electrochemical and morphological studies of formation of poly(4-hydroxybenzoic acid), prepared in different pH, on the graphite surface. Cyclic voltammetry, electrochemical impedance spectroscopy (EIS), electrochemical quartz crystal microbalance (EQCM) and atomic force microscopy (AFM) have been carried out to study the modified electrodes formed. The electrodes modified with poly(4-HBA), prepared in pH 0.5 and 7.0, presented oxidation/reduction peaks, but no peak was detected to modified electrodes prepared in pH 12.0. Voltammetric studies showed decrease in oxidation/reduction currents and slower electron transport across the polymer for all pH values, however, the electron transport was higher when the polymer was prepared in acid medium. EIS analysis indicated that the charge transfer resistance for poly(4-HBA) electropolymerized at pH 12.0 was about 2 and 1.4 times higher when compared to pH 0.5 and 7.0, respectively. Studies through EQCM showed higher amount of polymer mass deposited in acid medium. Images by AFM indicated that the topography is affected by pH value, whereas films prepared in acidic pH conditions presented higher roughness.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.