Abstract
The potential of rapid thermal processing (RTP) for the preparation of thin films of niobium oxynitrides was investigated. The 200 and 500 nm niobium films were deposited via sputtering on oxidized silicon(1 0 0)- and on sapphire(1 −1 0 2)-substrates. At first, oxidation of niobium films in molecular oxygen and then nitridation in ammonia using an RTP-system was performed. The films were characterized before and after the oxidation and nitridation processes by X-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM) and secondary ion mass spectrometry (SIMS). The influence of the two different substrates, amorphous SiO 2 and single crystalline sapphire on the reactivity of the niobium films was studied in dependence of temperature, time of reaction and film thickness. The existence of niobium oxynitride formation was verified for some of the films. In some of the experiments, crack formation in the films or even delamination of the Nb-films from the substrates was observed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.