Formation of Nanostructures in Severely Deformed High-Strength Steel Induced by High-Frequency Ultrasonic Impact Treatment

Abstract

Surface modification by the generation of a nanostructured surface layer induced via ultrasonic impact treatment was performed at the weld toe of a welded high-strength quenched and tempered structural steel, S690QL1 (Fe-0.16C-0.2Si-0.87Mn-0.33Cr-0.21Mo (wt pct)). Such high-frequency peening techniques are known to improve the fatigue life of welded components. The nanocrystallized structure as a function of depth from the top-treated surface was characterized via a recently developed automated crystal orientation mapping in transmission electron microscopy. Based on the experimental observations, a grain refinement mechanism induced by plastic deformation during the ultrasonic impact treatment is proposed. It involves the formation of low-angle misoriented lamellae displaying a high density of dislocations followed by the subdivision of microbands into blocks and the resulting formation of polygonal submicronic grains. These submicronic grains further breakdown into nano grains. The results show the presence of retained austenite even after severe surface plastic deformation. The average grain size of the retained austenite and martensite is $$\sim $$ 17 and $$\sim $$ 35 nm, respectively. The in-grain deformation mechanisms are different in larger and smaller grains. Larger grains show long-range lattice rotations, while smaller grains show plastic deformation through grain rotation. Also the smaller nano grains exhibit the presence of short-range disorder. Surface nanocrystallization also leads to an increased fraction of low angle and low energy coincident site lattice boundaries especially in the smaller grains ( $$D<50$$ nm).