Abstract
A nano decagonal quasicrystalline phase in the Al70Cu10Co5Ni15 alloy has been synthesized by mechanical alloying of a mixture of elemental powders followed by annealing. A high-energy ball milling of the elemental mixture of Al, Cu, Co and Ni leads to the formation of B2 type quaternary intermetallic alloys. The X-ray diffraction and transmission electron microscopy techniques have been employed for characterization of the samples. It was observed that the dissolution of the individual elements into an alloy led to the formation of a nano B2 phase. This phase was found to be quite stable against milling and no other crystalline or amorphous phases could be detected. Milled powder after annealing at 700 degrees C for 60 h was found to transform to nano-decagonal phase. Attempts have been made to understand the evolution of the complex intermetallic nano phases and their relative stability during milling.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.