Formation of metastable cubic-perovskite in high-pressure phase transformation of Ca(Mg, Fe, Al)Si2O6

Abstract

We have carried out in-situ X-ray diffraction experiments on high-pressure transformations of a Ca- and Fe- rich pyroxene (Ca 1 . 0 3 Mg 0 . 6 1 Fe 0 . 2 3 Al 0 . 1 4 Si 2 O 6 ) to investigate the stability of Ca 0 . 5 (Mg, Fe, Al) 0 . 5 SiO 3 perovskite (CM-perovskite) in a multi component system at about 32 GPa and up to 1900 °C. We observed that cubic CM-perovskite was formed at about 1300 °C and decomposed into cubic Ca-perovskites and orthorhombic Mg-perovskites and stishovite at 1800 °C when using a glass starting material. In another experiment using a crystalline pyroxene starting material, two cubic perovskites; Ca-perovskite and CM-perovskite, and orthorhombic Mg-perovskite formed simultaneously during the initial stage of the transformation. However, the cubic CM-perovskite subsequently decomposed into Mg- and Ca-perovskites and stishovite at 1200 °C. These results indicate that the assembly of cubic Ca-perovskite, orthorhombic Mg-perovskite and stishovite is stable and cubic CM-perovskite is a metastable phase at around 32 GPa and temperatures over 1000 °C in this system. Chemical analyses of product phases showed that Mg, Fe, and Al were preferentially partitioned into Mg-perovskite and the compositions of Ca-perovskite were close to pure CaSiO 3 . The present study shows that CM-perovskite nucleates during the initial stage of Ca(Mg, Fe, Al)Si 2 O 6 pyroxene transformation. Therefore, cold subducting slabs and impacted meteorites are the possible places in which CM-perovskite could exist. The Ca-rich glassy phase in a shocked chondrite (Tomioka and Kimura 2003) might have formed by vitrification of a metastable CM-perovskite-like phase.