Abstract
Low-dimensional quantum-well and nanoisland heterostructures formed in the InSb/AlAs system by molecular-beam epitaxy are studied by transmission electron microscopy and steady-state photoluminescence spectroscopy. The structures are grown under conditions of alternate In and Sb deposition (the socalled atomic-layer epitaxy mode) and the simultaneous deposition of materials (the traditional molecularbeam epitaxy mode). In both modes of growth, at a nominal amount of the deposited material in a single layer, large-sized (200 nm–1 μm) imperfect islands arranged on the In x Al1 – x Sb y As1–y quantum-well layer are formed. In the heterostructures grown under conditions of atomic layer epitaxy, the islands are surrounded by ring-shaped arrays of much smaller (~10 nm), coherently strained islands consisting of the In x Al1 – x Sb y As1 – y alloy as well. The composition of the alloy is defined by the intermixing of Group-V materials in the stage of InSb deposition and by the intermixing of materials because of the segregation of In and Sb atoms during overgrowth of the InSb layer by an AlAs layer.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.