Abstract
The non-oxidative decomposition of ethane to yield hydrogen and nanostructured carbon was carried out over a Ni–Cu–Al 2O 3 catalyst in a quartz fixed bed reactor. The effects of temperature, which ranged between 550 and 750 °C, on the gas product distribution, ethane conversion, hydrogen selectivity and carbon yield were investigated. Additionally, the effect of the space velocity on the catalytic decomposition of ethane over the Ni–Cu–Al 2O 3 was studied. At low temperatures and low space velocities, H 2 and CH 4 were the only gas products detected, although low ethane conversions were obtained. As the temperature was increased, both the ethane conversion and hydrogen selectivity increased, along with the production of ethylene as a by-product. High space velocities lead to low ethane conversions and hydrogen selectivities, although the carbon yield was significantly enhanced. A plausible mechanism of product formation under the operational conditions studied is presented. Characterization of the catalysts following reaction was performed with N 2 adsorption, XRD, SEM and TEM; the results suggested that carbon was mostly deposited as fishbone-like nanofibers that differed, based on the operational conditions, on the catalyst growth mode (bi-directional growth at low temperatures vs. mono-directional growth at higher temperatures) and on the structural degree of order (higher at high temperatures and low space velocities).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.