Abstract

This article discusses a method for forming black silicon using plasma etching at a sample temperature range from -20 °C to +20 °C in a mixture of oxygen and sulfur hexafluoride. The surface morphology of the resulting structures, the autocorrelation function of surface features, and reflectivity were studied depending on the process parameters-the composition of the plasma mixture, temperature and other discharge parameters (radical concentrations). The relationship between these parameters and the concentrations of oxygen and fluorine radicals in plasma is shown. A novel approach has been studied to reduce the reflectance using conformal bilayer dielectric coatings deposited by atomic layer deposition. The reflectivity of the resulting black silicon was studied in a wide spectral range from 400 to 900 nm. As a result of the research, technologies for creating black silicon on silicon wafers with a diameter of 200 mm have been proposed, and the structure formation process takes no more than 5 min. The resulting structures are an example of the self-formation of nanostructures due to anisotropic etching in a gas discharge plasma. This material has high mechanical, chemical and thermal stability and can be used as an antireflective coating, in structures requiring a developed surface-photovoltaics, supercapacitors, catalysts, and antibacterial surfaces.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.