Abstract
The effects of heating rate in the range of 0.3 to 693 °C/s on transformations during intercritical annealing of a cold-rolled 0.12C-1.4Mn-0.02Nb steel with either a ferrite-pearlite or ferrite-spheroidized carbide microstructure were evaluated. Heating rates were selected to impart different predicted degrees of ferrite recrystallization present at the onset of austenite formation. Rapid heating minimized ferrite recrystallization with both prior microstructures and minimized pearlite spheroidization in the ferrite-pearlite condition, and austenite formation occurred preferentially in recovered ferrite regions as opposed to along recrystallized ferrite boundaries. Martensite was evenly distributed in slowly heated steels because austenite formed on recrystallized, equiaxed, ferrite boundaries. With rapid heating, austenite formed in directionally oriented recovered ferrite, which increased the degree of banding. The greatest degree of banding was found with intermediate heating rates leading to partial recrystallization, because austenite formed preferentially in the remaining recovered ferrite, which was located in bands along the rolling direction. Ferrite-spheroidized carbide microstructures had somewhat reduced martensite banding when compared to the ferrite-pearlite condition, where elongated pearlite enhanced banded austenite leading to banding in transformed microstructures.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.