Abstract

TiO2 nanotube (TNT) arrays were formed by anodizing titanium foil in fluoride-ethylene glycol (EG) electrolyte added to it either water (H2O) or sodium hydroxide (NaOH) as oxidant. In NaOH added fluoride-EG electrolyte, 10 µm long TNT arrays were formed compared to 5 μm long nanotubes in H2O added fluoride-EG electrolyte. When NaOH was added to EG, the electrolyte pH was 9. As the pH of the electrolyte was rather high, surface etching of the nanotubes was reduced resulting in tubes with longer length. Moreover, the addition of NaOH into fluoride-EG resulted in the crystallization of anatase in the as-made TNT arrays. Annealing obviously improved the crystallinity of the oxide. The TNT arrays were then used as a photoanode in a dye-sensitized solar cell (DSSC). A photoconversion efficiency of 2.4 % was recorded with photocurrent of 6.9 mA/cm2.