Abstract
A hydroxyapatite (HAp) surface layer was generated at room temperature on a beta-titanium alloy (Ti-29Nb-13Ta-4.6Zr, TNTZ) using fine particle peening (FPP), as a means of enhancing fatigue resistance. This material is commonly employed in bio-implants, but has a suboptimal Young's modulus. Treated specimens were assessed using scanning electron microscopy, X-ray diffraction, energy dispersive X-ray spectroscopy and electron backscatter diffraction, as well as by measuring the Vickers hardness. Performing FPP using shot particles made of HAp was found to transfer the particles to the TNTZ surface to rapidly produce a HAp layer that became thicker as the FPP process progressed. Room-temperature four-point bending fatigue tests in air showed that the HAp layer resulting from the FPP process increased the endurance limit of test specimens. This improved performance is ascribed to the appearance of a hardened surface layer having a significant degree of compressive residual stress.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: International Journal of Lightweight Materials and Manufacture
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.