Abstract
The precipitation of the lamellar-shaped M 23C6 carbide within the dendritic matrix of a cobalt-base superalloy during thermal exposure at 1000 °C has been investigated. Such a precipitation is not commonly observed in cobalt-base superalloys. It is found that M 23C6 particles nucleate preferentially at stacking faults (SFs) in the dendritic matrix and grow along the SFs to develop a lamellar character. Additionally, a Cr depletion zone is observed in the vicinity of the lamellar M 23C6 carbide, which strongly supports the presence of Suzuki segregation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.