Formation and reduction behaviors of zirconium oxide compounds in LiCl–Li2O melt at 923 K

Abstract

The reduction behaviors of ZrO2, Li2ZrO3 and (U,Pu,Zr)O2 in a LiCl–Li2O salt bath at 923 K were investigated. This study was conducted as part of a feasibility study on the pyrochemical treatment of damaged fuel debris generated by severe accidents at light water reactors. It was demonstrated in electrolytic reduction tests that the uranium in synthetic corium specimens of (U,Pu,Zr)O2 with various ZrO2 contents could be reduced to the metallic form and that part of the zirconium was converted to Li2ZrO3. Zirconium metal and Li2ZrO3 were obtained by the reduction of ZrO2. The reduction of Li2ZrO3 did not proceed even in LiCl containing no Li2O. Moreover, the stable chemical forms of the ZrO2–Li2O complex oxide were investigated as a function of the Li2O concentration in LiCl. ZrO2 was converted to Li2ZrO3 at a Li2O concentration of 0.018 wt%. As the Li2O concentration was increased, Li2ZrO3 was converted to Li6Zr2O7 and then to Li8ZrO6. It is suggested that the removal of Li2ZrO3 from the reduction product is a key point in the pyrochemical treatment of corium.