Abstract

AbstractUnderstanding how the microstructure of the active Cu0 component in the commercially applicable Cu/ZnO/Al2O3(−Cs2O) low‐temperature water‐gas shift catalyst evolves under various H2 partial pressures in the presence/absence of a Cs promoter during thermal activation has been investigated. Time‐resolved XRD and spatially‐resolved XRD‐CT data were measured as a function of H2 concentration along a packed bed reactor to elucidate the importance of the zincite support and the effect of the promoter on Cu sintering mechanisms, dislocation character and stacking fault probability. The rate of Cu reduction showed a dependency on [Cs], [H2] and bed height; lower [Cs] and higher [H2] led to a greater rate of metallic copper nanoparticle formation. A deeper analysis of the XRD line profiles allowed for determining a greater edge character to the dislocations and subsequent stacking fault probability was also observed to depend on higher [H2], smaller Cu0 (and ZnO) crystallite sizes, increased [ZnO] (30 wt.%, sCZA) and lower temperature. The intrinsic activity of Cu/ZnO/Al2O3 methanol synthesis catalysts has been intimately linked to the anisotropic behaviour of copper, and thus the presence of lattice defects; to the best knowledge of the authors, this study is the first instance in which this type of analysis has been applied to LT‐WGS catalysts.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.