Abstract
FAMn:PbI3 perovskite films were synthesized and probed mainly through electron spin resonance (ESR) spectroscopy. FAMn:PbI3 with low (~1%) Mn concentration showed a hyperfine sextet line originated from Mn++ ions. FAMn:PbI3 with high (10%) Mn concentration showed broad resonance (~500 G peak-to-peak linewidth). However, after bombardment of FAMn:PbI3 with high Mn concentration by focused ion beams (FIB), a sharp ESR peak appeared. The peak-to-peak linewidth (ΔHpp) was ~8 G regardless of the temperature. The FIB-induced defect showed Curie behavior at low temperatures (5 K - 50 K), which indicates the presence of localized electrons at the defect sites at low temperatures. The g-value increased from g = 2.0002 to 2.0016 as the temperature increased from 5 K to 50 K. Together with the ongoing search for electron spin echo (ESE), this could potentially provide a platform for realizing magnetic bits, information storage, and increased manipulation speed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.