Abstract
Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) samples were successfully foamed using supercritical carbon dioxide as a physical foaming agent. PHBV sheets were first saturated at 175 °C followed by a foaming process at different temperatures (145 to 165 °C) and different CO2 pressures (10 to 29 MPa). It was found that microcellular structures with average cell sizes ranging from 6 to 22 μm and cell densities ranging from 108 to 1.2 × 109 cells/cm3 could be controllably prepared by selecting suitable foaming conditions. To investigate crystallization behavior during the foaming process and explore the corresponding foaming mechanism, differential scanning calorimetry, wide angle X-ray diffraction, and small-angle X-ray scattering characterizations were carried out. Stretching behavior during the cell growth stage may increase the crystal nucleation rate, and the generated crystal nucleus accelerates the crystallization rate as well as thickens PHBV crystal lamellae.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.