Fluorescence spectroscopic study of dip coated sol-gel thin film internal environment using fluorescent probes Hoechst33258 and Pyranine

Abstract

The characterization of physicochemical properties of the internal environment of sol-gel thin films is required for understanding and designing applications in optical biosensors. We have investigated the dip coated tetraethyl-orthosilicate (TEOS) derived sol-gel thin films deposited on microscopic glass cover slips using molar ratio (water or ethanol / TEOS) R=32 using fluorescence spectroscopic measurements (emission, lifetime and anisotropy) on entrapped fluorescent probes. The effect of water and/or ethanol was studied as a function of storage (60 days) using fluorescent probes Hoechst 33258 (H258) and Pyranine (PY). Distribution of fluorescent probes in thin film was studied using confocal microscope. Emission maxima of H258 entrapped thin films from sol prepared using water as solvent showed emission maximum at 503 nm indicating the presence of water like environment which did not change during storage. On the contrary, PY entrapped thin films depicted emission bands at 434 nm and 513 nm, characteristics of ethanol and water respectively, up to the first few weeks and then the band at 434 nm prevailed (60 days), suggesting heterogeneous internal environment. Thin films from sol prepared using ethanol as solvent showed presence of ethanol through out storage. Fluorescence lifetime data of these probes in both sol-gel and thin films also suggested presence of heterogeneous internal environment. Thin films prepared from sol-gel using water as solvent suggested release of ethanol in the pores during hydrolysis and condensation reaction, which were clearly indicated by PY. The effect of sodium phosphate buffer was also studied in sol-gel and thin films. The results of these measurements showed that both the probes H258 and PY could be used effectively in monitoring the physicochemical properties of internal environment of thin films and sol-gel as a function of storage.