Abstract
To research the dispersion properties and infrared (IR) interference efficiency of graphite flake particulates modified by hydrophobic nano-silica, the flowability of graphite flake particles before and after modification was measured by a powder property tester. The smoke was formed by dispersing the graphite flake particles into the smoke box using air flow dispersion way. The mass concentration and IR spectrum transmission of the smoke were measured. On the basis of stir settlement model, the settling velocity of smoke was calculated. Results show that the Carr′s flowability index of graphite flake particulates modified with hydrophobic nano-silica in mass ratio of 4.0 % is the highest, reaching 61 and at the same time, the settling velocity decreases from 2.288×10 -3 m·s -1 before modification to 1.125×10 -3 m·s -1 after modification. Average IR spectrum transmission of the smoke formed in the wave band range of 3-5 μm and 8-12 μm decreases from 0.3895 % and 0.7288% to 0.072% and 0.176%. The physical modification of hydrophobic nano-SiO 2 on graphite flake surface effectively improves the flowability and dispersion properties and significantly increases the duration of the smoke formed by graphite flake particles and IR interference performance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.