Abstract
To study the weld line formation of colliding flow fronts the filling of a mold cavity was simulated. The thermo-rheological findings were used to investigate the sources of weld line weakness. In this way critical areas of the interface in regard to the lack of interdiffusion and the inappropriate molecular orientation were found to be placed near the surface of the finished parts. The main source for the weld line weakness seems to be the V-notch that arises due to the poorly bonded region near the surface in combination with the large shrinkage as a result of extremely high molecular orientations induced at the end of the filling. Furthermore, the empirical knowledge was confirmed that weld lines are rather more sensitive to the local flow situation than the global processing conditions. Melt and mold temperatures can be considered to be the most important factors which influence the weld line strength.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.