Abstract
ABSTRACTThe most commonly used lead-free solders contain large amounts of tin, which makes them incompatible with the conventional Cu-based underbump metallization (UBM) schemes. The tin in the solder reacts with the copper layer of the UBM, depleting the UBM of copper and causing loss of adhesion and a weak interface. Use of new under bump metallization schemes with Ni or CuNi alloys as the solderable layer were investigated in this study. Instead of Cr, a Tibased adhesion layer was used to decrease the amount of stress in the CuNi layer. Flip chip solder joints were made in which three Sn-Bi-Ag based lead-free solders were reflowed to several UBM pads of different compositions. The resulting interfacial microstructures were examined by SEM/EDX analysis of cross-sectioned samples. The joints were also mechanically tested in fatigue and shear to assess the quality and reliability of the interface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.