Flexural properties untreated and treated kenaf fiber reinforced polypropylene composites

Abstract

Today natural fiber polymer composites are being extensively used as alternatives in producing furniture to fulfill society demand instead of saving cost and environmentally friendly. The objective of this search is to investigate the untreated fine and rough kenaf fiber (KF) as well as treated KF reinforced with polypropylene (PP) on the flexural strength. Flexural strengths of pure PP, 10%, and 20% of untreated fine and rough KF by weight to PP have been recorded. In addition, flexural strengths of treated KF soaked with 5% and 10% of Sodium Hydroxide (NaOH) have also been recorded. KF reinforced PP (PP/KF) untreated and treated composites were melt blended and then injection molded to observe their flexural strengths by measuring their threshold. Three point bending test was apply to determine the flexural stress of the composites. The result show treated fine KF produce better flexural performance at 20% PP/KF. Scanning Electron Microscopy (SEM) is used to observe the morphological surface PP/KF. Overall 5% NaOH with 20% PP/KF (Fine KF) show good interfacial bonding PP/KF and best result with flexural stress value 30.25MPa.Today natural fiber polymer composites are being extensively used as alternatives in producing furniture to fulfill society demand instead of saving cost and environmentally friendly. The objective of this search is to investigate the untreated fine and rough kenaf fiber (KF) as well as treated KF reinforced with polypropylene (PP) on the flexural strength. Flexural strengths of pure PP, 10%, and 20% of untreated fine and rough KF by weight to PP have been recorded. In addition, flexural strengths of treated KF soaked with 5% and 10% of Sodium Hydroxide (NaOH) have also been recorded. KF reinforced PP (PP/KF) untreated and treated composites were melt blended and then injection molded to observe their flexural strengths by measuring their threshold. Three point bending test was apply to determine the flexural stress of the composites. The result show treated fine KF produce better flexural performance at 20% PP/KF. Scanning Electron Microscopy (SEM) is used to observe the morphological surface PP/KF. Over...