Flexural properties of blockboard reinforced with glass fiber and various types of fabrics

Abstract

Flexural properties were evaluated of blockboard with spruce (Picea abies Mill) core and faces made of 2.5-mm fromager (Ceiba pentandra) veneer and 3-mm high-density fiberboard (HDF). For these two types of structures, fiber glass, jute, gauze, and cotton fabrics, were separately bonded under the face layers to improve the strength performance. Flexural properties, modulus of rupture (MOR), and modulus of elasticity (MOE) were determined under laboratory conditions. Improved values were found for MOR and MOE tested in the parallel to core grain direction compared to those perpendicular-to-grain. They were 32% to 49% (MOR) and 39% to 95% (MOE) improvements in case of veneer faces and 142% to 161% (MOR) and 134% to 245% (MOE) improvements in case of HDF faces. The best results of MOR and MOE were obtained for glass fiber used as insertion material, the higher ones being reached for specimens tested in the parallel direction to grain, which were 56.1 N/mm2 (MOR) and 6704 N/mm2 (MOE) for HDF faces. Generally, the improvements were more evident on the blockboard structures with veneer faces oriented perpendicular-to-core grain (30% for MOR and 18% MOE) and for HDF faces with parallel core grain orientation (16% for MOR and 6% MOE).